Proteksi Katodik Menggunakan Zinc Anode Untuk Menghambat Korosi Pada Lambung Kapal Port Link Vii Jakarta

Teddy Ihza Mahendra; Dwisetiono Dwisetiono

doi:10.62012/zl.v3i2.19694

Authors

Teddy Ihza Mahendra Universitas HangTuah
Dwisetiono Dwisetiono Universitas HangTuah

DOI:

https://doi.org/10.62012/zl.v3i2.19694

Keywords:

Proteksi Katodic, Zinc Anode

Abstract

Cathodic protection is a thermodynamic corrosion rate control method by treating metal structures as cathodes. Cathodic protection is very important to reduce the corrosion rate of the underwater surface area of the hull plate. This protection is affixed to parts of the ship that are susceptible to seawater corrosion, more precisely located below the water line. Most of the damage to the ship's steel construction plate is caused by the corrosion process. As a result of this corrosion causes substantial material losses, so protection is needed to prevent corrosion by using cathodic methods. Basically, corrosion control methods can be grouped into two groups, namely kinetic methods and thermodynamic methods. In the kinetic method of controlling corrosion, it is done by providing barriers to the interaction with the environment so that the corrosion rate can be reduced, but the tendency for corrosion to occur itself is not resolved, so that if the obstacles are removed corrosion will take place again soon. The application of cathodic protection is often combined with coatings. Its purpose is to protect the steel when the coating is damaged

Downloads

Download data is not yet available.

References

B. Sudjasta, P. J. Suranto, and H. Setiani, “ANALISIS KEBUTUHAN PEMASANGAN ZINK ANODE UNTUK MENCEGAH KOROSI PADA LAMBUNG KAPAL KAPAL GENERAL CARGO,” Bina Tek., vol. 14, no. 2, pp. 209–215, 2018.

P. A. Schweitzer, “Corrosion of Linings and Coatings, Cathodic and Inhibition Protection and Corrosion Monitering.” Taylor & Francis Group, New York, 2007.

S. Jatmiko, “STUDI KOMPARASI PROTEKSI KATHODIK ANTARA ANODA ZINK DENGAN ANODA ALUMINIUM SETELAH DIAPLIKASIKAN PADA TUG BOAT UNIVERSAL DAN TUG BOAT MARINER,” Kapal, 2009.

R. W. Revie and H. H. Uhlig, “Iron and Steel,” Corros. Corros. Control an Introd. to Corros. Sci. Eng. 4th ed. Hoboken Wiley-Interscience, 2008.

F. E. Blount, “Electrochemical Prinsiples of Cathodic Protection Corrosion Control.” NACE, 1989.

B. Utomo, “Jenis korosi dan penanggulangannya,” vol. 6, no. 2, pp. 138–141, 2009.

T. Karyono, B. Budianto, and R. G. Pamungkas, “ANALISIS TEKNIK PENCEGAHAN KOROSI PADA LAMBUNG KAPAL DENGAN VARIASI SISTEM PENCEGAHAN ICCP DIBANDINGKAN DENGAN SACP,” J. Pendidik. Prof., vol. 6, no. 1, 2017.

J. R. Davis, Corrosion: Understanding the basics. Asm International, 2000.

M. Tanaka and H. D. Bui, Inverse Problems in Engineering Mechanics: IUTAM Symposium Tokyo, 1992. Springer Science & Business Media, 2013.

H. D. Bui, M. Tanaka, M. B. A. H. MAIGRE, E. LUZZATO, and M. REYNIER, “Inverse Problems in,” Eng. Mech., 1994.

T. Rachman, “Analysis Of Laying And The Need For Cathodic Protection On Single Point Mooring Type Catenary Anchor Leg Mooring Buoy 035 Owned By PT. Pertamina Fuel Terminal Tuban”, mp, vol. 1, no. 1, pp. 41-46, Feb. 2022.

I. Utami, “Proteksi Katodik Dengan Anoda Tumbal Sebagai Pengendalian Korosi Baja Dalam Lingkungan Aqueous,” J. Tek. Kim., vol. 3, no. 2, pp. 240–245, 2012.

I. Utami, “PROTEKSI KATODIK DENGAN ANODA TUMBAL SEBAGAI PENGENDALI LAJU KOROSI BAJA DALAM LINGKUNGAN AQUEOUS.”

S. Soeryanto, A. A. Mashuri, and B. Samudra, “Proses Repairing Ponton di PT. Dok dan Perkapalan Surabaya,” Otopro, vol. 12, no. 2, p. 50, 2019, doi: 10.26740/otopro.v12n2.p50-57.