KONDISI OPTIMUM PROSES KEMPA PANAS DALAM PEMBUATAN PAPAN PARTIKEL DENGAN PEREKAT KITOSAN
DOI:
https://doi.org/10.24259/perennial.v15i2.7650Kata Kunci:
chitosan, particle board, temperature and pressing time, hot pressAbstrak
Shrimp skin contains chitin that is the second largest biopolymer after cellulose. The chitin can be isolated to produce chitosan. Chitosan is a natural adhesive that can be applied in producing particleboards to substitute formaldehyde-based adhesives. The purpose of this study was to analyze the hot-pressing condition in term of temperature and pressing time on the physical and mechanical properties of the particleboards produced by using chitosan as adhesives. The particleboards were made with the size of 25x25x0.7 cm and target density of 0.75 g/cm3. The particleboards were produced using different temperatures (160ºC, 180ºC, and 200ºC) and pressing times (9, 12, and 15 minutes. The results showed that the chitosan produced met the standards, and temperature and compression time had a significant interaction effect on the thickness swelling and modulus of elasticity. The optimum combination of temperature and pressing time is 180ºC and 12 minutes, respectively. The produced boards have the characteristics of moisture content 12.2%, density 0.81, water absorption 84.47%, thickness swelling 19.73%, modulus of rupture 143.36 kg/cm2, modulus of elasticity 23,367.79 kg/cm2, and internal bonding 9.03 kg/cm2.Unduhan
Referensi
Agustina, S., Swantara, I., & Suartha, I. (2015). Isolasi kitin, karakterisasi, dan sintesis kitosan dari kulit udang. Jurnal Kimia, 9(2), 271–278.
Badan Standarisasi Nasional. (2006). SNI Papan Partikel (Nomor 03-2105-2006). Bogor: Badan Standarisasi Nasional.
Bowyer, J. L., R. Shmulsky, and J. G. Haygreen. (2003). Forest products and wood science: an introduction (4th ed.). Iowa, USA: Iowa State Press.
Dompeipen, E.J., Marni, K., & Riadi, P.M. (2016). Isolasi kitin dan kitosan dari limbah kulit udang. Majalah BIAM, 12 (1): 32-38.
Fauziah, Wahyuni, D., & Lapanporo, B.P. (2014). Analisis sifat fisik dan mekanik papan partikel berbahan dasar sekam padi. Positron, 4(2): 60-63.
Hossain, M.S., & Iqbal, A.. (2014). Production and characterization of chitosan from chrimp waste. J. Bangladesh Agril. Univ., 12 (1): 153- 160.
Japanese Standards Association. (2003). Particleboards (JIS A 5908: 2003). Tokyo, Japan: Japanese Standards Association.
Kusumaningsih, T., Masykur, A., & Arief, U. (2004). Pembuatan kitosan dari kitin cangkang bekicot. Jurnal Biofarmasi, 2(2): 64-68.
Prayitno, T.A., Widyorini, R., & Rofii, M.N. (2008). Kualitas perekatan dua jenis kayu hutan rakyat dengan variasi perlakuan panas (Laporan Penelitian Tahun 2008). Retrived from https://repository.ugm.ac.id/96969/1/Kualitas%20Perekatan%20Dua%20Jenis%20Kayu%20Hutan%20Rakyat%20Dengan%20Variasi%20Perlakuan%20Panas.pdf
Roffael, E. (1993). Formaldehyde Release from Particle Board And Other Wood Based Panels. Kuala Lumpur, Malaysia: Forest Research Institute Malaysia.
Saputro A.N.C., Indriana K., & Sutarno. (2009). Pengaruh metode isolasi terhadap sifat karakteristik kitosan. Prosiding Seminar Nasional Kimia dan Pendidikan Kimia 2009. Surakarta, 18 Maret 2009: Program Studi Pendidikan Kimia, Jurusan Matematika dan Ilmu Pengetahuan Alam, Fakultas Keguruan dan Ilmu Pendidikan, Univesitas Sebelas Maret Surakarta
Setiawan, C.N.B. (2004). Pemanfaatan tandan kosong kelapa sawit sebagai bahan baku perekat likuida kayu dan papan partikel berkerapatn sedang (Skripsi). Bogor: Fakultas Kehutanan Institut Pertanian Bogor.
Sudiryanto, G. (2015). Pengaruh suhu dan waktu pengempaan terhadap sifat fisik dan mekanik papan partikel kayu sengon (Paraserienthes falcatria). Jurnal DISPROTEK, 6 (1): 67-74.