ELECTRODEPOSITION OF Cu ON THE SURFACE OF SILICA FREE RICE HUSK ACTIVATED CARBON WITH ULTRASONIC IRRADIATION

Ryan Andhika; Muhammad Zakir; Maming Maming

doi:10.20956/ica.v8i2.2471

Submitted

Sep 15, 2017

Accepted

Sep 15, 2017

Published

Dec 1, 2015

Download

PDF

Statistic

Read Counter : 266 Download : 0

Downloads

Download data is not yet available.

Abstract

Electrodeposition of Cu on the surface of silica free rice husk activated carbon with ultrasonic irradiation aimed to increase the value of specific capacitance was carried out. Silica free rice husk activated carbon was synthesized using H3PO4 activator and extraction of silica using KOH. The surface area of rice husk carbon was obtained before and after the extraction of silica and after activation were 57.2833 m2/g, 180.5378 m2/g and 184.6074 m2/g, respectively. XRF analysis showed that Cu depositioned on the surface of silica free rice husk activated carbon and based of CV measurements showed that electrodeposition of Cu with ultrasonic irradiation can increased the value of specific capacitance. Specific capacitance of silica free rice husk activated carbon before and after electrodeposition of Cu with ultrasonic irradiation were 657.75 nF/g and 721.08 nF/g, respectively.

Keywords

Cuprum electrodeposition specific capacitance activated carbon ultrasonic.

How to Cite

Andhika, R., Zakir, M., & Maming, M. (2015). ELECTRODEPOSITION OF Cu ON THE SURFACE OF SILICA FREE RICE HUSK ACTIVATED CARBON WITH ULTRASONIC IRRADIATION. Jurnal Akta Kimia Indonesia (Indonesia Chimica Acta), 8(2), 29-37. https://doi.org/10.20956/ica.v8i2.2471

Download Citation

References

Agung, M.G.F., Hanafie, S.M.R. dan Mardina, P., 2013, Ekstraksi Silika dari Abu Sekam Padi dengan Pelarut KOH, Konversi, 2 (1), 28-31.
Andaka, G., 2008, Penurunan Kadar Tembaga pada Limbah Cair Industri Kerajinan Perak dengan Presipitasi menggunakan Natrium Hidroksida, J. Teknol., 1 (2), 127-134.
Ariyanto, T., Prasetyo, I. dan Rochmadi, 2012, Pengaruh Struktur Pori terhadap Kapasitansi Elektroda Superkapasitor yang dibuat dari Karbon Nanopori, Reaktor, 14 (1), 25-32.
Dell, R.M. and Rand, D.A.J., 2001, Energy Storage-A Key Technology for Global Energy Sustainability, J. Power Sources, 100, 2-7.
Frackowiak, E. and Beguin, F., 2001, Carbon Materials for The Electrochemical Storage of Energy in Capacitors, Carbon, 39, 937-950.
Gao, Y., Li, L., Jin, Y., Wang, Y., Yuan, C., Wei, Y., Chen, G., Ge, J. and Lu, H.,
, Porous Carbon Made from Rice Husk as Electrode Material for Electrochemical Double Layer Capacitor, Appl. Energy, 153, 41-47.
Herniyanti, S., Taer, E. dan Sugianto, 2014, Pengaruh Aktivasi Karbon Dioksida pada Produksi karbon Aktif Monolit dari Kayu Karet, JOM FMIPA, 1 (2), 205-210.
Himmaty, I. dan Endarko, 2013, Pembuatan Elektroda dan Perancangan Sistem Capacitive Deionization untuk Mengurangi Kadar Garam pada Larutan Sodium Clorida (NaCl), Berkala Fisika, 16 (3), 67-74.
Karyasa, I.W., 2014, Pembuatan Ultra Fine Amorphous Silica (UFAS) dari Jerami Padi dan Sekam Padi, J. Sains Teknol., 3 (1), 263-274.
Kasuma, N.Y., 2012, Penggunaan KompositZnO-CuO yang disintesis secara Sonochemistry yang digunakan sebagai Katalis untuk Fotodegradasi Metil Orange dan Zat Antibakteri, Tesis diterbitkan, Program Studi Kimia, Pascasarjana, Universitas Andalas, Padang.
Koleangan, H.S.J. dan Wuntu, A.D., 2008, Kajian Stabilitas Termal dan Karakter Kovalen Zat Pengaktif pada Arang Aktif Limbah Gergajian Kayu Meranti (Shorea spp), Chem. Prog., 1 (1), 43-46.
Mahvi, A.H., Maleki, A. and Eslami, A., 2004, Potential of Rice Husk Ash for Phenol Removal in Aqueous Systems, Am. J. Appl. Sci., 1 (4), 321-326.
Mujiyanti, D.R., Nuryono dan Kunarti, E.S., 2010, Sintesis dan Karakterisasi Silika Gel dari Abu Sekam Padi yang diimobilisasi dengan 3-(Trimetoksisilil)-1-Propantiol, Sains Ter. Kim., 4 (2), 150-167.
Rahmawati, F., Wahyuningsih, S. dan Handayani, N., 2008, Modifikasi Permukaan Lapis Tipis Semikonduktor TiO2 Bersubstrat Grafit dengan Elektrodeposisi Cu, Indo. J. Chem., 8 (3), 331-336.
Ramdja, A.F., Halim, M. dan Handi, J., 2008, Pembuatan Karbon Aktif dari Pelepah Kelapa (Cocus nucifera), J. Tek. Kim.,15 (2), 1-8.
Rizki, A., Taer, E. dan Rika, 2015, Kebolehulangan (Reproducibility)
dalam Pembuatan Sel Superkapasitor dari Kayu Karet, JOM FMIPA, 2 (1),
-101.
Shofa, 2012, Pembuatan Karbon Aktif Berbahan Baku Ampas Tebu dengan Aktivasi Kalium Hidroksida, Skirpsi diterbitkan, Program Studi Teknik Kimia, Fakultas Teknik, Universitas Indonesia, Depok.
Sugiyono, A., Permana, A.D., Boedoyo, M.S. dan Adiarso, 2013, Outlook Energi Indonesia 2013: Pengembangan Energi dalam Mendukung Sektor Transportasi dan Industri Pengolahan Mineral, Pusat Teknologi Pengembangan Sumber Daya Energi, Jakarta. Suhada, H., 2001, Fuel Cell sebagai Penghasil Energi Abad 21, J. Tek. Mesin, 3 (2), 92-100.
Surest, A.H., Kasih, J.A.F. dan Wisanti, A., 2008, Pengaruh Suhu, Konsentrasi Zat Aktivator dan Waktu Aktivasi terhadap Daya Serap Karbon Aktif dari Tempurung Kemiri, J. Tek. Kim., 15 (2), 17-21.
Suslick, K.S., Hyeon, T. and Fang, M., 1996, Nanostructured Materials Generated by High-Intensity Ultrasound: Sonochemical Synthesis and Catalytic Studies, Chem. Mater., 8, 2172-2179.
Suwandana, R.F. dan Susanti, D., 2015, Analisis Pengaruh Massa Reduktor Zinc terhadap Sifat Kapasitif Superkapasitor Material Graphene, J. Tek. ITS, 4 (1), 95-100.
Triastuti, W.E. dan Purwanto, D.B., 2012, Efek Penambahan Ion Tartrate terhadap Elektrodeposisi Mn-Cu pada Pipa Baja Karbon, Kapal, 9 (3), 167- 170.
Vytras, K., Svancara, I. and Metelka, R., 2009, Carbon Paste Electrodes in Electroanalytical Chemistry, J. Serb. Chem. Soc., 74 (10), 1021-1033.
Wachid, M.R. dan Setiarso, P., 2014, Pembuatan Elektroda Pasta Karbon Termodifikasi Bentonit untuk Analisis Ion Logam Tembaga(II) secara Cyclic Voltammetry Stripping, Prosiding Seminar Nasional Kimia, Universitas
Negeri Surabaya, Surabaya, 20 September.
Wei, X., Xiao, L., Jin, Z. and Ping, Z.S., 2011, Nanoporous Carbon Derived from Rice Husk for Electrochemical Capacitor Application, Adv. Mater. Res., 239-242.
Zakir, M., Botahala, L., Ramang, M., Fauziah, S. dan Abdussamad, B., 2013, Elektrodeposisi Logam Mn pada Permukaan Karbon Aktif Sekam Padi dengan Iradiasi Ultrasonik, Indo. Chim. Acta, 6 (2), 9-
Zakir, M., Maming, Raya, I., Karim, A. dan Santi, 2012, Pemanfaatan Energi Gelombang Ultrasonik dalam Adsorpsi Ion Logam Berat Cu(II) pada Biosorben Karbon Aktif dari Sekam Padi, Indo. Chim. Acta, 5 (2),
-9.

References

Agung, M.G.F., Hanafie, S.M.R. dan Mardina, P., 2013, Ekstraksi Silika dari Abu Sekam Padi dengan Pelarut KOH, Konversi, 2 (1), 28-31.

Andaka, G., 2008, Penurunan Kadar Tembaga pada Limbah Cair Industri Kerajinan Perak dengan Presipitasi menggunakan Natrium Hidroksida, J. Teknol., 1 (2), 127-134.

Ariyanto, T., Prasetyo, I. dan Rochmadi, 2012, Pengaruh Struktur Pori terhadap Kapasitansi Elektroda Superkapasitor yang dibuat dari Karbon Nanopori, Reaktor, 14 (1), 25-32.

Dell, R.M. and Rand, D.A.J., 2001, Energy Storage-A Key Technology for Global Energy Sustainability, J. Power Sources, 100, 2-7.

Frackowiak, E. and Beguin, F., 2001, Carbon Materials for The Electrochemical Storage of Energy in Capacitors, Carbon, 39, 937-950.

Gao, Y., Li, L., Jin, Y., Wang, Y., Yuan, C., Wei, Y., Chen, G., Ge, J. and Lu, H.,

, Porous Carbon Made from Rice Husk as Electrode Material for Electrochemical Double Layer Capacitor, Appl. Energy, 153, 41-47.

Herniyanti, S., Taer, E. dan Sugianto, 2014, Pengaruh Aktivasi Karbon Dioksida pada Produksi karbon Aktif Monolit dari Kayu Karet, JOM FMIPA, 1 (2), 205-210.

Himmaty, I. dan Endarko, 2013, Pembuatan Elektroda dan Perancangan Sistem Capacitive Deionization untuk Mengurangi Kadar Garam pada Larutan Sodium Clorida (NaCl), Berkala Fisika, 16 (3), 67-74.

Karyasa, I.W., 2014, Pembuatan Ultra Fine Amorphous Silica (UFAS) dari Jerami Padi dan Sekam Padi, J. Sains Teknol., 3 (1), 263-274.

Kasuma, N.Y., 2012, Penggunaan KompositZnO-CuO yang disintesis secara Sonochemistry yang digunakan sebagai Katalis untuk Fotodegradasi Metil Orange dan Zat Antibakteri, Tesis diterbitkan, Program Studi Kimia, Pascasarjana, Universitas Andalas, Padang.

Koleangan, H.S.J. dan Wuntu, A.D., 2008, Kajian Stabilitas Termal dan Karakter Kovalen Zat Pengaktif pada Arang Aktif Limbah Gergajian Kayu Meranti (Shorea spp), Chem. Prog., 1 (1), 43-46.

Mahvi, A.H., Maleki, A. and Eslami, A., 2004, Potential of Rice Husk Ash for Phenol Removal in Aqueous Systems, Am. J. Appl. Sci., 1 (4), 321-326.

Mujiyanti, D.R., Nuryono dan Kunarti, E.S., 2010, Sintesis dan Karakterisasi Silika Gel dari Abu Sekam Padi yang diimobilisasi dengan 3-(Trimetoksisilil)-1-Propantiol, Sains Ter. Kim., 4 (2), 150-167.

Rahmawati, F., Wahyuningsih, S. dan Handayani, N., 2008, Modifikasi Permukaan Lapis Tipis Semikonduktor TiO2 Bersubstrat Grafit dengan Elektrodeposisi Cu, Indo. J. Chem., 8 (3), 331-336.

Ramdja, A.F., Halim, M. dan Handi, J., 2008, Pembuatan Karbon Aktif dari Pelepah Kelapa (Cocus nucifera), J. Tek. Kim.,15 (2), 1-8.

Rizki, A., Taer, E. dan Rika, 2015, Kebolehulangan (Reproducibility)

dalam Pembuatan Sel Superkapasitor dari Kayu Karet, JOM FMIPA, 2 (1),

-101.

Shofa, 2012, Pembuatan Karbon Aktif Berbahan Baku Ampas Tebu dengan Aktivasi Kalium Hidroksida, Skirpsi diterbitkan, Program Studi Teknik Kimia, Fakultas Teknik, Universitas Indonesia, Depok.

Sugiyono, A., Permana, A.D., Boedoyo, M.S. dan Adiarso, 2013, Outlook Energi Indonesia 2013: Pengembangan Energi dalam Mendukung Sektor Transportasi dan Industri Pengolahan Mineral, Pusat Teknologi Pengembangan Sumber Daya Energi, Jakarta. Suhada, H., 2001, Fuel Cell sebagai Penghasil Energi Abad 21, J. Tek. Mesin, 3 (2), 92-100.

Surest, A.H., Kasih, J.A.F. dan Wisanti, A., 2008, Pengaruh Suhu, Konsentrasi Zat Aktivator dan Waktu Aktivasi terhadap Daya Serap Karbon Aktif dari Tempurung Kemiri, J. Tek. Kim., 15 (2), 17-21.

Suslick, K.S., Hyeon, T. and Fang, M., 1996, Nanostructured Materials Generated by High-Intensity Ultrasound: Sonochemical Synthesis and Catalytic Studies, Chem. Mater., 8, 2172-2179.

Suwandana, R.F. dan Susanti, D., 2015, Analisis Pengaruh Massa Reduktor Zinc terhadap Sifat Kapasitif Superkapasitor Material Graphene, J. Tek. ITS, 4 (1), 95-100.

Triastuti, W.E. dan Purwanto, D.B., 2012, Efek Penambahan Ion Tartrate terhadap Elektrodeposisi Mn-Cu pada Pipa Baja Karbon, Kapal, 9 (3), 167- 170.

Vytras, K., Svancara, I. and Metelka, R., 2009, Carbon Paste Electrodes in Electroanalytical Chemistry, J. Serb. Chem. Soc., 74 (10), 1021-1033.

Wachid, M.R. dan Setiarso, P., 2014, Pembuatan Elektroda Pasta Karbon Termodifikasi Bentonit untuk Analisis Ion Logam Tembaga(II) secara Cyclic Voltammetry Stripping, Prosiding Seminar Nasional Kimia, Universitas

Negeri Surabaya, Surabaya, 20 September.

Wei, X., Xiao, L., Jin, Z. and Ping, Z.S., 2011, Nanoporous Carbon Derived from Rice Husk for Electrochemical Capacitor Application, Adv. Mater. Res., 239-242.

Zakir, M., Botahala, L., Ramang, M., Fauziah, S. dan Abdussamad, B., 2013, Elektrodeposisi Logam Mn pada Permukaan Karbon Aktif Sekam Padi dengan Iradiasi Ultrasonik, Indo. Chim. Acta, 6 (2), 9-

Zakir, M., Maming, Raya, I., Karim, A. dan Santi, 2012, Pemanfaatan Energi Gelombang Ultrasonik dalam Adsorpsi Ion Logam Berat Cu(II) pada Biosorben Karbon Aktif dari Sekam Padi, Indo. Chim. Acta, 5 (2),

-9.

ELECTRODEPOSITION OF Cu ON THE SURFACE OF SILICA FREE RICE HUSK ACTIVATED CARBON WITH ULTRASONIC IRRADIATION

Article Sidebar

Downloads

Main Article Content

Abstract

Keywords

Article Details

References

References